摘要：The Ce2SO4/H2O2 containing solution is used to prepare a chrome-free cerium oxide based chemical conversion coating on AZ91D magnesium alloy at room temperature,and an orthogonal experiment was carried out to optimize the treating process.The effect of preparing parameters on the coating growth and the corrosion resistance were studied.It was found that H2O2 is the dominant influence factor on the coating weight gain in the orthogonal experiment,with Ce(SO4)2 coming next and immersion time having the least impact,while the most dominant influence factor on the corrosion resistance is Ce(SO4)2,with H2O2 coming next and immersion time having the least impact.The coating has the best corrosion resistance,treated in the solution of 10 g/l Ce(SO4)2 and 12 ml/l H2O2 for 4 min.SEM was adopted to study the micro-morphology of the conversion coating on magnesium alloy surface The prolonged immersion time duration or the increased concentration of Ce(SO4)2 and H2O2 will increase the coating thickness,but tiny cracks appears resulted from the fast coating deposition.
注：因版权方要求，不能公开全文，如需全文，请咨询杂志社