作者：BaoMing-dong; XuJin-fu; XuXue-bo; ZouG...镍合金烧结硬质合金工具钢无定形合金炽烧
摘要：Cemented Carbide YG11C and Tool Steel Crl2MoV was blazed with Ni-base amorphous alloys, QG-1011,MBF-20 and MBF-75, using dynamics thermodynamics analogue testing machine Gleeble 1500D. The effects of brazing temperature, holding time and holding pressure on micro-structure and bond strength were investigated. Results showed that YG11C and Cr12MoV were all wetted well by these three Ni-base alloys, and the bond strength was as high as 220MPa,320MPa, 320MPa respectively. When the blazing temperature was at the point over the melting point 60-70℃ of Ni-base alloy, the holding time was about 2-10min, the suitable pressure was benefit for improving the brazing quality.Microanalysis showed Co in cemented carbide diffused into liquid brazing alloy and formed the Fe-Co solid .solution.