作者：TomaszBabul; NataliaKucharieva; Aleksa...氮碳共渗工具钢加工动力学渗碳层厚度显微硬度磨损
摘要：The paper presents the results of wear and metallography tests of tool steel grades: ASTM A681, Chl2M and Ch12FS per GOST, AMS 6437E i BS X46Cr13, all surface hardened by the Carbo process (carburizing) and by the NiCar process (nitrocarburizing). The thermo-chemical treatment was conducted in powder pack for a duration of 6 h (carburizing)and for 4 h in the case of nitrocarburizing. Factors investigated were: morphology, depth and microhardness of the cases obtained, their microstructure, as well as phase composition. Wear tests were conducted by the three cylinder-cone method.Wear velocity was 0.58 m/s, unit load was 50 MPa and 400Mpa, wear path was 3470 m. Oil SAE30 was applied at the rate of 30 drops per minute.